FEATURES
- Std Roll Length: 72.00 yards
- 430 acrylic adhesive
- Closed cell crosslinked polyethylene foam
- Thickness nominal = 31.0 mil.
- Thickness tolerance = 25.0 mil. - 45.0 mil.
- Approximate density (foam only) = 6 lb./ft. to the 3rd power
- Static shear 1/2in. squared overlap will hold 1000 gms at 72°F for 10,000 min.
- Dynamic Shear = 55 lb./in. squared
- Maximum length = 175 yds.
- Roll width = 1600.0 mil. - 480.0 mil.
- Slitting tolerance = +/ - 31.0 mil.
ADVANTAGES
- No apparent degradation when exposed for seven days in the UV chamber
- No apparent degradation when exposed to splash testing of typical hydrocarbon solvents
- No cracking when flexed around a 1/4in. mandrel during a cold flex test at -20°F
APPLICATIONS
MARKETS SERVED
COLORS
|
 |
GENERAL INFORMATION
| A 31.0 mil. double coated polyethylene foam tape with 430 acrylic adhesive is ideal for joining, mounting, gasketing and sealing applications involving irregular surfaces. 4492B tape combines a conformable closed cell foam with a high strength acrylic adhesive that provides good initial tack and offers high ultimate adhesion to a wide variety of surfaces. 430 is a firm acrylic pressure-sensitive adhesive which features good initial adhesion and good resistance to both elevated temperatures and environmental conditions. Solvent splash testing cycle = 20 seconds submersion and 20 seconds air dry through 3 cycles. Slit rolls 1/8in. up to 1/2in. are only available in standard lengths. Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improve bond strength. To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified. Typical surface cleaning solvents are isopropyl alcohol and water (rubbing alcohol) or water. Be sure to follow the manufacturer's precautions and directions for use when using cleaning solvents. Initial tape application below 50°F is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory. |
|
| PRODUCT CONSTRUCTION |
| |
Type |
Mil Thickness |
|
 |
| Backing |
PE - Polyethylene |
|
| Adhesive (unwind) |
Acrylic |
|
| Adhesive (liner) |
Acrylic |
|
| Liner Type (outer) |
Paper (3.0 mil., tan) |
|
| Liner Type (inner) |
Papre (3.0 mil., tan) |
|
| Foam Cell Type |
Closed |
|
| Thickness (total) |
|
31.00 |
|
|
| PRIMARY PHYSICAL PROPERTIES |
| |
Unwind Side |
|
Liner Side |
|
|
| Adhesion-to-Steel - 90° Peel |
128.00 oz/in |
|
128.00 oz/in |
| Adhesive Activation |
Pressure |
|
|
| Adhesive Thermal Conductive |
No |
|
|
| Tensile Strength |
60.00 lbs/in |
|
|
Testing Info: Peel Adhesion: ASTM D3330 72 hour dwell at R.T., 90° angle peel, 12 in./min. jaw speed; Static Shear: ASTM D3654; Tensile: ASTM D897, 72 hour dwell, (T-Block), 1in. squared, jaw speed 2 in./min.; Dynamic Shear: ASTM D1002 |
|
|
| SECONDARY PHYSICAL
PROPERTIES |
| UV Resistant |
Yes |
| Solvent Resistant |
Yes |
|
|
| THERMAL / ELECTRICAL
PROPERTIES |
| Minimum Application Temperature |
50°F |
| Minimum Service Temperature |
0°F |
| Maximum Long-Term Temperature |
158°F |
| Maximum Short-Term Temperature |
180°F |
|
|
|